Product introduction:
The soft felt is manufactured through the following process: it is laid in specifc layers, then glued, hot-pressed, and cured to form a green body. Subsequently, the green body undergoes carbonization, high-temperature treatment, purifcation, and machining to produce the fnal product.
Product advantages:
Ablation Resistance and Low Coeffcient of Thermal Expansion / Low Thermal Conductivity and Excellent Thermal Insulation Performance
|
Density g/cm3 |
Bending Strength MPa |
Tensile Strength Mpa |
Compressive Strength Mpa |
Interlayer Shear Strength Mpa |
Resistivity um·Ω |
Thermal Conductivity (Vertical Direction) W/m·K |
Ash Content ppm |
Graphitization Temperature ℃ |
Size mm |
| 0.13-0.16 | 0.65 | / | 0.3 | / | / | 0.12-0.16 | ＜20 | ＞2200 | l≤2000 |
The above data are representative values and are not guaranteed values.