Product Introduction:
Barrel-shaped products with high strength, high modulus and stable physical and chemical properties are prepared by winding and laying non-woven fabrics/woven fabrics and fber mats, combined with needle-punching technology, and densifed through a process that integrates gas-phase infltration and liquid-phase impregnation.
Product advantages:
Excellent ablation resistance and strong corrosion resistance / High strength and long service life.
Production process:
Blank - Machining - Finished Product.
Single-Crystal Furnace Heater, High-Temperature Heat Treatment Heater
|
Density g/cm3 |
Bending Strength MPa |
Tensile Strength Mpa |
Compressive Strength Mpa |
Interlayer Shear Strength Mpa |
Resistivity um·Ω |
Thermal Conductivity (Vertical Direction) W/m·K |
Ash Content ppm |
Graphitization Temperature ℃ |
Size mm |
| 1.5 | 140 | 160 | 135 | 20 | 20 | 8 | ≤200 | ≥2000 | d≤1500 |
The above data are representative values and are not guaranteed values.