Product Introduction:
Carbon-carbon fasteners are made through the following process: preforms are formed by alternately laying continuous long-fber non-woven fabrics and fber mat fabrics for reinforcement. These preforms then undergo a combined gas-liquid process to become carbon-carbon blanks, which are subsequently precision-ma-chined into various carbon-carbon fasteners.
Product advantages:
Short production cycle / High strength, suitable for use in high-temperature environments / Excellent ablation resistance and strong corrosion resistance.
Production process:
Blank - Machining - Finished Product
|
Density g/cm3 |
Bending Strength MPa |
Tensile Strength Mpa |
Compressive Strength Mpa |
Interlayer Shear Strength Mpa |
Resistivity um·Ω |
Thermal Conductivity (Vertical Direction) W/m·K |
Ash Content ppm |
Graphitization Temperature ℃ |
Size mm |
| 1.4 | 125 | 160 | 130 | 20 | / | 8 | ≤200 | ≥2000 | l≤2000 |
The above data are representative values and are not guaranteed values.