Product introduction:
Special-shaped carbon-carbon materials with high strength, high modulus and stable physical and chemical properties are prepared by winding and laying non-woven fabrics/woven fabrics and fber mats, combined with needle-punching technology, and densifed through a process that integrates gas-phase infltration and liquid-phase impregnation.
Product advantages:
Light in texture, convenient for tooling disassembly and cleaning / Good thermal shock resistance / Slow thermal conductivity with energy consumption saving effect.
Production process:
Preform Blank - Gas-Phase/Liquid-Phase Densifcation - High-Temperature Treatment - Machining - Finished Product
Inner Support Rod for Single-Crystal Furnace
|
Density g/cm3 |
Bending Strength MPa |
Tensile Strength Mpa |
Compressive Strength Mpa |
Interlayer Shear Strength Mpa |
Resistivity um·Ω |
Thermal Conductivity (Vertical Direction) W/m·K |
Ash Content ppm |
Graphitization Temperature ℃ |
Size mm |
| 1.3 | 90 | 130 | 120 | 25 | / | 6 | ≤200 | ≥2000 | l≤1400 |
The above data are representative values and are not guaranteed values.