Product Introduction:
Carbon-carbon plates with high strength, high modulus and stable physical and chemical properties are prepared by laminating non-woven fabrics/woven fabrics and fber mats, combined with needle-punching technology, and densifed through a process that integrates chemical vapor infltration (CVI) and liquid impregnation.
Product advantages:
Short production cycle / Slow thermal conductivity / Long service life / Excellent ablation resistance and strong corrosion resistance.
Production process:
Blank - Machining - Finished Product.
Inner Support Ring and Chassis Protection for Single-Crystal Furnaces
|
Density g/cm3 |
Bending Strength MPa |
Tensile Strength Mpa |
Compressive Strength Mpa |
Interlayer Shear Strength Mpa |
Resistivity um·Ω |
Thermal Conductivity (Vertical Direction) W/m·K |
Ash Content ppm |
Graphitization Temperature ℃ |
Size mm |
| 1.5 | 180 | 165 | 140 | 20 | 18 | 8.5 | ≤200 | ≥2000 | d≤2000 |
The above data are representative values and are not guaranteed values.